Oligomers And Polymers Containing Sulfinate Groups And Method For The Production Thereof

ABSTRACT

The invention relates to novel polymers or oligomers containing at least sulfinate groups (P-(SO2)nX, X=1-(n=1), 2-(n=2) or 3-(n=3) valent metal cation or H+ or ammonium ion NR4+ where R=alkyl, aryl, H), which are obtained by completely or partially reducing polymers or oligomers containing at least SO2Y-groups (Y═F, Cl, Br, I, OR, NR2 (R=alkyl and/or aryl and/or H), N-imidazolyL N-pyrazolyl) by means of suitable reducing agents in a suspension or in a solution form 
     Polymer and polymer(blend)membranes which are obtained by further reacting the received sulfinated polymers, especially by alkylation of the sulfinate groups with mono- di- or oligo functional electrophiles. The invention further relates to methods for producing the sulfinated polymers and for further reacting the sulfinated polymers with electrophiles by S-alkylation.

It is known from the literature that in polymers containing sulfinate groups SO2Li the sulfinate groups can be cross-linked by di- or oligohalogenoalkanes with alkylation of the sulfinate group to the sulfone group¹. This crosslinking method can be used to cross-link ionomer membranes in order to reduce the membrane swelling which leads to a better mechanical and thermal stability of the membranes in the respective membrane process (for example electrodialysis, diffusion dialysis, membrane fuel cells (hydrogen membrane fuel cells, direct methanol fuel cells)). One can produce two different types of in such a way cross-linked ionomer membranes:

1) The sulfonated polymer is dissolved together with the sulfinated polymer in a suitable, often dipolar aprotic solvent and a dihalogeno cross-linker or oligohalogeno cross-linker if necessary is added, for example 1,4-diiodobutane. During the solvent evaporation the cross-linking reaction takes place². ¹ “Vernetzung von modifizierten Engineering Thermoplasten” J. Kerres, W. Cui, W. Schnurnberger: Deutsches Patent 196 22 337.7 (Anmeldung vom 4. 6. 1996), Deutsches Patentarnt (1997) “Reticulation de Materiaux Thermoplastiques Industriels Modifies”J. Kerres, W. Cui, W. Schnurnberger: Französisches Patent F 97 06706 vom 30.05.1997 “Cross-Linking of Modified Engineering Thermoplastics” J. Kerres, W. Cui, W. Schnurnberger: U.S. Pat. No. 6,221,923; erteilt arn 24.4.2001² “Development and Characterization of Crosslinked Ionomer Membranes Based Upon Sulfinated and Sulfonated PSU. 2. Crosslinked PSU Blend Membranes By Alkylation of Sulfinate Groups With Dihalogenoalkanes.” Jochen Kerres, Wei Cui, Martin Junginger J. Memb. Sci. 139, 227-241 (1998)

2) A polymer, which contains both sulfinate and sulfonate group (produced by partial oxidation, for example, of the polymeric sulfinate with NaOCl, KMnO₄, H₂O etc.), is dissolved in a suitable dipolar aprotic solvent and a dihalogeno cross-linker or oligo halogeno cross-linker if necessary is added, for example 1,4-diiodobutane. During the solvent evaporation the cross-linking reaction takes place³. Up to now however only sulfinated polymers are known from the literature, which are prepared from the reaction of organometallated polymers with Sulphur dioxide (for example lithiated polysulfone from the reaction of polysulfone with butyl- or phenyllithium)^(4,5). However, not every type of polymers can be treated with organometallic reagents since the organometallic reagents react with functional groups of the polymers and are able to destroy the polymers. Organometallic reagents react with the carbonyl group, for example, so that high performance thermoplastics of the polyetherketone family containing the carbonyl group in the main chain for example (Polyetherketone PEK Victrex ®, polyetheretherketone PEEK Victrex ®, polyetheretherketoneketone PEEKK or polyetherketoneetheretherketone (PEKEKK Ultrapek ®)) can not be sulfinated via lithiation. For the introduction of the sulfinate group, another way must be found for these polymers. It would be desirable to have sulfinated polyetherketones, since these polymer could then be cross-linked. The polyetherketones are thermally and mechanically more stable than for example polysulfones or polyphenyleneethers, and therefore cross-linked ionomer membranes from polyetherketone polymers might show better stabilities in (electro)membrane processes. ³ “New sulfonated engineering polymers via the metalation route. 2. Sulfinated-Sulfonated Poly(ethersulfone) PSU Udel® and Its Crosslinking.” J. Kerres, W. Zhang, W. Cui J. Polym. Sci.: Part A: Polym. Chem. 36, 1441-1448 (1998)⁴ “Aromatic Polysulfone Compounds and their Manufacture” M. D. Guiver, O. Kutowy U.S. Pat. No. 4,999,415 (1991)⁵ “Aromatische Polysulfonderivate und Verfahren zu ihrer Herstellung” M. D. Guiver, O. Kutowy, J. W. ApSimon Patentanmeldung-Offenlegungsschrift DE 36 36 854 A1 (1987)

From the literature it is known that low-molecular sulfochlorides can be reduced to sulfinates by reduction with Zn dust, iron dust, sodium sulfite, hydrazine, H₂S, LiAlH₄, triethylaluminium, ethylaluminium sesquichloride^(6,7). The reduction leads to good yields primarily with Zn dust⁸ and with LiAlH₄ ⁹. It was surprisingly found now that polymers, which contain non-ionic sulfonate group derivatives, e. g. the sulfochloride group SO₂Cl, (polymeric sulfochlorides are easily accessibly by reaction of the sulfonic acid group with thionyl chloride, phosphorous trichloride oxide, phosphorous pentoxide or by reaction of lithiated polymers with sulfinyl chloride), can be converted with suitable reducing agents or with mixtures of suitable reducing agents in solution or in suspension in high yield and without cross-linking. The sulfochloride group of the respective polymers can be converted to sulfinate group either completely or partially, depending on type and quantity of reducing agent and or other reaction conditions (e.g. concentration, temperature). The fact that no cross-linking of the polymer as a side reaction takes place during the reduction is primarily remarkable and therefore surprising since it is known for example of sulfinic acids that these can react under disproportionation with each other. It was particularly surprising that the reaction of the polymeric sulfochlorides took place with LiAlH₄ at temperatures of −20 to −60° C. without cross-linking and with a high yield, since at this reaction lewis acidic intermediates appear, which could catalyse the cross-linking of the formed sulfinate group⁹.

It was further surprising that at the reduction of polymeric sulfochlorides with aqueous sodium salt solutions or other sulphurous reducing agents like sodium dithionite, sodium thiosulfate or mixtures of these reducing agents the reaction can be controlled in such a way, that only a part of the sulfochloride groups is converted to sulfinate groups, and the remaining sulfochloride groups remain unchanged (e. g. are not hydrolyzed to the sulfonic acid group). This is of importance when the sulfinate groups of the polymers containing both sulfochloride and sulfinate groups are alkylated by S-alkylation. Examples of alkylations are: ⁶ “Syntheses of sulfinic acids” Uri Zoller, in “The Chemistry of Sulphinic Acids, Esters and Their Derivatives”, ed. by S. Patai, John Wiley and Sons, 1990, New York, S. 187f⁷ “VIII. Reductions of Sulfonyl Derivatives” S. Oae, in “Organic Sulfur Chemistry: Structure and Mechanism”, ed. by J. T. Doi, CRC Press, Inc., Boca Raton, 1991, S. 334f⁸ “Sodium p-Toluenesufinate” F. C. Whitmore, F. H. Hamilton, in “Organic Syntheses”, Coll. Vol. I, ed by H. Gilman, 2nd ed., John Wiley and Sons, New York, 1956⁹ “Lithium Aluminium Hydride Reduction of Certain Sulfonic Acid Derivatives” L. Field, F. A. Grunwald J. Org. Chem. 16, 946-953 (1951)

-   -   covalent crosslinking with dihalogeno or oligohalogeno compounds         or other difunctional or oligofunctional alkylation agents         or/and     -   Reaction with monofunctional alkylation agents.

The sulfinate S-alkylation apparently proceeds in a greater yield if sulfochloride groups are available in the polymer instead of ionical sulfonic acid salt derivatives. The reason for this is presumably, that unloaded sulfochloride groups are solvated better than sulfonate salt groups by the solvents, which are used normally for polymers containing sulfinate groups (dipolar aprotic solvents like N-methylpyrrolidinone NMP, N,N-dimethylacetamide DMAc, N,N-dimethylformamide DMF, dimethylsulfoxide DMSO or sulfolane). A better solvation leads to a better solubility of both the sulfochlorinated polymer and the sulfinated polymer (ion effect: if the ion concentration and with that the ionic strength of the solution containing the different polymers is smaller, the sulfinated polymer is also dissolved better) and thus to higher reactivity of the polymer (polymers) containing sulfinate groups with the alkylation agents.

With the method of the present invention a large number of polymeric sulfinates according to the invention becomes accessible—actually every polymer or oligomers sulfonic acid can be transferred after transformation into the sulfohalide or another non-ionic sulfonic acid derivative to the respective polymeric or oligomeric sulfinate. Thus particularly sulfinated polymers become accessible, which can not be sulfinated by other methods, such as e.g. polymers containing carbonyl groups in the main chain or in the side chain. Particularly the high performance thermoplastics from the family of the polyetherketones which can not be lithiated can be sulfinated according to the present invention.

Thus also new covalent crosslinked oligomers or polymers or polymer(blend)membranes for most different applications become accessible, for example for membrane processes like membrane fuel cells, electrodialysis (if necessary with bipolar membranes), pervaporation, gas separation, diffusion dialysis, reverse osmosis, perstraction etc.

The special advantage of the reduction process of the present invention consists in that it is possible to reduce the sulfonyl groups only partially by a lower than equimolar amount of reducing agent so that polymer or oligomers which carry both sulfinate and sulfonyl groups on the same backbone are obtained. The sulfonyl groups can be hydrolyzed acidically, alkaline and/or neutral to the respective sulfonate group in another step, so that an oligomer or polymer which contains both sulfonate and sulfinate group arises, can be converted in a further step to covalently crosslinked proton-conducting polymer membranes, whereby the sulfinate group can be crosslinked according to usual methods¹.

Another possibility for the preparation of polymeric sulfohalides, which are only partially reduced to sulfinate is made possible by the use of polymers carrying two or three different sulfohalide groups on the same polymer backbone. Particularly preferred are combinations from sulfochlorides, sulfobromides and/or sulfofluorides. Especially preferred are combinations from sulfochloride and sulfobromide group in the same polymer molecule. The ratios of the sulfohalide groups can be every arbitrary value between each other. Depending on the chosen reducing agent and the solvent used the corresponding sulfohalides show a different tendency towards reduction.

The preparation of polymers which comprise sulfohalides and sulfinate groups on the same backbone is particularly preferred as mentioned above already. Followed by a further processing to a membrane which is covalently crosslinked as it is shown exemplarily in the example 5 with the polymer PEEK. After the crosslinking the remaining sulfohalide group is alternatively hydrolyzed in water, a diluted acid and/or alkaline and transferred into the sulfonic acid or sulfonic acid salt derivative.

The ratio of sulfochloride to sulfinate group in the end product can accept every arbitrary value. It is only and alone dependent on the chosen reduction conditions. Being included

a) the duration of the reduction: it is between few seconds up to 60 hours, 10 to 30 hours are preferred

b) the temperature of the reduction: It is depending on medium between −60° C. and 100° C. Using sodium sulfit as a reducing agent it is between 50° C. and 100° C.

c) the solvents used: preferred are water and dipolar-aprotic solvents, particularly preferred are dipolar-aprotic polar solvents (as NMP, DMAc, DMSO and THF) and arbitrary mixtures of the solvents with each other.

While the reduction of the sulfinated oligomers and polymers according to the invention is carried out, other alkylation agents apart from the di- or oligofunctional crosslinker (for example 1.4 diiodobutane) can be added at the same time to the solution of the sulfinated polymer/oligomer in a suitable solvent, which alkylate sulfinate groups simultaneously with the cross-linking reaction. Thereby crosslinked membranes and other formed objects can be produced, whose properties are modified by the additionally introduced functional groups. If the other alkylation agents contain acidic functions, for example, a cation conductivity, particularly a proton conductivity, of the crosslinked membranes and others polymer formed object can be generated. An alkylation with alkylation agents containing basic groups leads to membranes modified with basic anion-exchange groups.

The main chains (backbones) of the polymers and oligomers of the present invention are arbitrarily chosen, however, the following polymers are preferred, as main chains:

-   -   Polyolefines like polyethylene, polypropylene, polyisobutylene,         polynorbornene,     -   Polymethylpentene, polyisoprene, poly (1.4 butadiene), poly (1.2         butadiene)     -   Styrene(co)polymer like polystyrene, poly(metylstyrene),         poly(α,β,β-triflourostyrene), poly (pentaflourostyrene)     -   perflourinated ionomers like Nafion® or the SO2Hal-precursor of         Nafion® (Hal═F, Cl, Br, I), Dow® membrane, GoreSelect® membrane     -   sulfonated PVDF and/or the SO2Hal-precursor, whereby Hal stands         for fluorine, chlorine, bromine or iodine     -   (Hetero) aryl main chain polymers like:         -   Polyetherketones like polyetherketone PEK Victrex ®,             polyetheretherketone PEEK Victrex ®,             polyetheretherketoneketone PEEKK,             polyetherketoneetherketoneketone PEKEKK Ultrapek ®         -   Polyethersulfones like polysulfone Udel®, polyphenylsulfone             Radel R®, Polyetherethersulfone Radel A®, polyethersulfone             PES Victrex ®         -   Poly(benz)imidazole like PBI Celazol® and other oligomers             and polymers containing the (Benz) imidazole monomer whereby             the (Benz)imidazole group can be present in the main chain             or in the polymer lateral chain         -   Polyphenyleneether like e.g. poly(2,6-dimethyloxyphenylene),             poly(2,6-diphenyloxyphenylene)         -   Polyphenylenesulfide and copolymeres         -   Poly (1,4-phenylene) or poly (1,3phenylene), which can be             modified in the lateral group, if necessary with benzoyl,             naphtoyl or o-phenyloxy-1,4-benzoyl group, m             phenyloxy-1,4-benzoyl groups or p-phenyloxy-1,4-benzoyl             groups.         -   Poly (benzoxazole) and copolymers         -   Poly (benzthiazole) and copolymers         -   Poly (phtalazinone) and copolymers         -   Polyaniline and copolymers

The reaction equations (1) and (2) show exemplary the reduction of sulfonated PEEK (polyetheretherketone) to the sulfinate:

The partial reduction of sulfonated PEEK is exemplarily represented in the following flowchart over the corresponding sulfochloride to the sulfinate.

As polymeric sulfinates are very unstable the resulting sodium salt form is transferred into the considerably more stable lithium salt by cation exchange.

According to the method of the present invention is the partial or complete reduction of sulfochlorinated polysulfone (PSU) or other poly(ethersulfone)s and sulfochlorinated PEEK or other poly(etherketone)s is quite particularly preferred.

The membranes produced by covalent crosslinking can be applied to hydrogen fuel cells, particularly in membrane fuel cells, in a temperature range of −50° C. to +280° C. depending on the main polymer backbone.

EXAMPLES

1. Preparation of a sulfinated polysulfone PSU Udel ® by reduction of PSU sulfochloride with lithiumaluminiumhydride 10.83 g sulfochlorinated PSU Udel ® are dissolved in 300 ml of tetrahydrofurane (THF). The solution is cooled down under argon protective gas to −65° C. After this 13 ml of a 0.013 molar lithiumalminiumhydride solution in THF are added within 2 hours via a dropping funnel into the polymer solution. The beginning of the reduction is indicated by hydrogen development. After the hydrogen development is finished, what is the case after about 1 hour, a mixture of 60 ml of 10 per cent LiOH solution and 120 ml ethanol is injected into the reaction mixture. After this the reaction mixture is precipitated into 2.5 l iso-propanol and filtered. The residue is dried at 60° C. in the drying oven at 50 hPascal pressure. The formation of the PSU sulfinate is observed by an IR spectrum of the product. The sulfinate band at 970 cm⁻¹ is considerably recognizable (illus. 1, IR spectra of PSU-SO₂Cl (spectrum 1) made by reaction of PSU-Li with SO₂ (spectrum 2) of PSU-SO₂Li and made by reduction of PSU-SO₂Cl with LiAlH₄ (spectrum 3) of PSU-SO₂Li.

2. Preparation of sulfinated poly (etheretherketone) PEEK by reduction of PEEK-SO₂Cl with aqueous sodium sulfit solution

-   Material: -   7.6 g PEEK-SO₂Cl (0.02 mol) -   126 g of (1 mol) Na₂SO₃ -   500 ml H2O

PEEK-SO₂Cl+Na₂SO₃+H₂O→PEEK-SO₂Na+NaCl+NaHSO₄

PEEKSO₂Cl is added to 500 ml of a 2M Na₂SO₃ solution and is stirred at 70° C. for 20 hours. After this it is heated up to 100° C. and allowed to react for 10 min at this temperature. Then the white polymer is filtered off. The polymer is then stirred in 500 ml of a 10% LiOH solution to transform the sulfinate group into the Li form by ion-exchange. After this it is filtered and the precipitate is washed up to the neutral reaction of the washing water. After this the polymer is dried at room temperature up to weight constancy under vacuum. After this the polymer is suspended in water and dialysed. The dialysed polymer solution is dehydrated and the polymer dried at room temperature and vacuum up to the weight constancy.

IR:The band of the suinate group SO₂Li is detected easily at 970 cm-1 (illus. 2).

The sulfinated PEEK is easily soluble in NMP and DMSO. If 1,4-diiodobutane is given to a NMP solution of the polymer, within 5 min. a gelation takes place and with that a crosslinking of the polymer. Illus. 4 shows a 1-H-NMR spectium of the sulfinated PEEK.

Elemental analysis: 1,0 groups replaced.

C H S Cl Theo. 63.69 3.07 8.94 0 Exp. 52.52 3.71 6.60 1.95

Elemental analysis after dialysis of the product polymer (there is still Cl present in the polymer as sulfochloride):

C H S Cl Theo. 63.69 3.07 8.94 0 Exp. 53.26 4.09 6.89 2.01

Elemental analysis of the starting product sulfochlorinated PEEK:

C H S Cl Theo. 59.06 2.85 8.29 9.07 Exp. 57.43 3.07 8.32 9.54

Elemental analysis with calculated values if 25% of the functional groups are present as a sulfochloride and 75% of the functional groups as a sulfinate would be:

Molecular mass 397 g/mol. (C₁₉H₁₁O₇S₁Cl_(0.25)Li_(0.75))

C H S Cl Theo. 57.31 2.77 8.06 2.20 Exp. 52.52 3.71 6.60 1.95

3. Preparation of partly sulflnated poly (etheretherketone) PEEK by reduction of PEEK-SO₂Cl with aqueous sodium sulfite solution

-   Material: -   20 g PEEK-SO₂-Cl (0.053 mol) -   300 ml of 2 molar aqueous solutions of Na₂SO₃

PEEK-SO₂Cl+Na₂SO₃+H₂O→PEEK SO₂Na+NaCl+NaHSO₄

PEEKSO₂Cl is added to 300 ml of a 2M Na₂SO₃ solution and is stirred at 70° C. for 20 hours. Then the white polymer is filtered off. The polymer is then stirred in 500 ml of a 10% LiOH solution to bring the sulfinate group in the Li form. After this it is filtered and the precipitate is washed up to the neutral reaction of the washing water. After this the polymer is dried at room temperature up to weight constancy under vacuum. After this the polymer is suspended in water and dialysed. The dialysed polymer solution is dehydrated and the polymer dried at room temperature and vacuum up to weight constancy.

Elemental analysis results after dialysis:

C H S Cl Theo. 63.69 3.07 8.94 0 Exp. 56.21 4.00 6.75 2.55

The elemental analysis result corresponds to about 0.28 remaining sulfochloride group and 0.72 obtained sulfinate group per repeating unit. A redox titration of the sulfinated polymer with a surplus of NaOCl and back titration with sodium thiosulfate yields about 0.58 sulfinate group per repeating unit.

-   Data of the titration: -   C_(Na2S203)=0,1N -   C_(NaOCl)=0.4962 mmol/g -   1,259 g PEEK-SO₂Li -   11,265 g NaOCl(5,5897 mmol) -   V_(Na25203)=70,626 ml -   G_(NaOCl)=70,626*0, ½=3,53133 mmol -   G_(SO2Li)=5,5897-3,5313=2,0584 mmol -   40° C., 4 Stunden. 150 ml H₂O.

IEC_(Peek-SO2Li)=2,0584/1,259=1,63 mmol/g (approximately 0.58 SO₂Li groups per repeating unit).

The oxidized polymer is titrated with 0.1 N NaOH. It results an IEC of 2.52 meq SO₃H groups per g of polymers. The starting polymer sulfonated PEEK (before sulfochloride formation) had an IEC of 2.7 meq/g.

4. Production ofpartially reduced PEEK-SO₂Cl

-   Material: -   7.6 g PEEK-SO₂Cl (0.02 mol) -   126 g of (1 mol) Na₂SO₃ -   500 ml H₂O

PEEK-SO₂Cl+Na₂SO₃+H₂O→ClO₂S-PEEK-SO₂Na+NaCl+NaHSO₄

PEEKSO₂Cl is added to 300 ml of a 2M Na₂SO₃ solution and is stirred at 70° C. for 20 hours. Then the white polymer is filtered off. The polymer is then stirred in 500 ml of a 10% LiOH solution to bring the sulfinate group in the Li form. After this it is filtered and the precipitate is washed up to the neutral reaction of the washing water. After this the polymer is dried at room temperature up to weight constancy under vacuuum. After this the polymer is suspended in water and dialysed. The dialysed polymer solution is dehydrated and the polymer dried at room temperature and vacuum up to the weight constancy. The obtained product contains both sulftnate and sulfochloride groups.

5. Preparation of covalently crosslinked membranes by using sulfinated PEEK The sulfinated PEEK from example 3 (0.72 sulfinate group and 0.28 sulfochloride group per repeating unit) is dissolved, if necessary together with sulfonated PEK-SO₃Li (for IEC_(sPEK)=1.8 meq/g), in NMP to give a 15% solution. The crosslinker 1,4-diiodobutane is added to the solution, and a membrane is cast. The solvent is evaporated in the vacuum drying oven (first 100° C./800 hpas, then 120° C./50 hpas), and the membrane taken out of the drying oven. After cooling, it is removed under water, posttreated in 7% NaOH at 60° C. for 1 day, followed by water at 90° C. for 1 day, then in 10% H₂SO₄ at 90° C. for 1 day, and finally in water at 90° C. for 1 day.

Membrane preparation:

Membrane Sulfinated Sulfonated NMP 1,4-diiodobutane [no.] PEEK [g] * PEK [g] ** [g] [ml] PEEK 1 1 2 20 0.23 PEEK 2 1 1 20 0.24 PEEK 3 1 — 10 0.1 * Sulfinated PEEK from example 3 ** 1.8 = meq SO₃Li/g of polymers sulfonated PEEK with IEC

Characterization results of the membranes:

Extraction Membrane IECexp. IECtheo Water Rsp residue [no.] [meq/g] [meq/g] uptake [%] [Ω*cm]* [%]** PEEK-1 1.61 1.53 76.2 4.2 — PEEK-2 1.4 1.4 85.9 5.13 39.4 PEEK-3 1.01 1.0 18.1 22.1 100 *measured in 0.5 N HCl, impedance at room temperature (25° C.) **stored in 90° C. hot DMAc, residue centrifuged off, washed with MeOH and water and dried in vacuum at increased temperature

One sees from illus. 6, that the swelling of the covalently crosslinked membrane from PEEK-SO₂Li SO₂Cl (PEEK which contains both sulfochloride and sulfinate group) is even at a temperature of 90° C. only 33%, and this at a high proton conductivity of 22.1 Ω*cm. This is a remarkable result which lets expect for this membrane very good prospects at the application into membrane fuel cells at T>80° C.

Following in the scheme the formation of the covalent crosslinked membrane from partially reduced PEEK-SO₂Cl:

The polymers particularly preferred in the context of the invention are shown with their structures on the following pages once again. The shown polymers are substituted with sulfohalide groups prior to the reduction. The substitution degree per recurring unit is different from polymer to polymer and can reach values up to 10 sulfohalide groups per repeating unit. Values of 1 to 5, particularly of 2 to 4 sulfohalide groups are preferred. 100% of the sulfohalide groups can be reduced to sulfrnate groups, however, a partial reduction of the sulfohalide groups to sulfmate groups is preferred. A value of 30 to 60% of the used sulfohalide groups is preferred.

For the preparation of covalent membranes from polymers that carry both sulfohalide and sulfochloride groups, membranes are preferred, that have an ion exchange capacity (IEC) of 0.8 to 2.2 after the hydrolysis, membranes with an IEC from 1.0 to 1.8 are particularly preferred. 

1. At least sulfinate group (P-(SO₂)nX, X=1-(n=1), 2-(n=2) or 3-(n=3) valent metal cation or H+ or ammonium ion NR₄ ⁺ with R=alkyl, aryl, H) containing polymer or oligomer in the volume or at the surface, characterized in that it is obtained by a complete or partial reduction of a polymer or oligomer containing SO₂Y groups (Y═F, Cl, Br, I, OR, NR₂ (R=alkyl and/or aryl and/or H), (N imidazole, N pyrazole) by means of suitable reducing agents in suspension or in solution either in the volume or superficially.
 2. Polymer or oligomer or polymer(blend)membrane containing sulfinate groups P-(SO₂) nX) according to claim 1 characterized in that the polymer or oligomer is selected from the groups of: Polyolefines like polyethylene, polypropylene, polyisobutylene, polynorbornene, Polymethylpentene, polyisoprene, poly(1,4butadiene), poly(1,2-butadiene) Styrene(co)polymers like polystyrene, poly(metylstyrene), poly(α,β,β-triflourostyrene), poly(pentaflourostyrene) perfluorinated ionomers like Nafion® or the SO₂Hal-precursor of Nafion® (Hal═F, Cl, Br, I), Dow® membrane, GoreSelect® membrane (Hetero) aryl main chain polymers like: Polyetherketones like polyetherketone PEK Victrex ®, polyetheretherketone PEEK Victrex ®, polyetheretherketoneketone PEEKK, polyetherketoneetherketoneketone PEKEKK Ultrapek ® Polyethersulfones like polysulfone Udel®, polyphenylsulfone Radel R®, Polyetherethersulfone Radel A®, polyethersulfone PES Victrex ® Poly(benz)imidazole like PBI Celazol® and other oligomers and polymers containing the (Benz)imidazole monomer whereby the (Benz)imidazole group can be present in the main chain or in the polymer lateral chain Polyphenyleneethers like e.g. poly(2,6-dimethyloxyphenylene), poly(2,6-diphenyloxyphenylene) Polyphenylenesulfide and copolymers Poly (1,4-phenylene) or poly (1,3-phenylene), which can be modified in the lateral group, if necessary with benzoyl, naphtoyl or o-phenyloxy-1,4-benzoyl group, m phenyloxy- 1,4benzoyl groups or p-phenyloxy-1,4benzoyl groups, Poly (benzoxazole) and copolymers Poly (benzthiazole) and copolymers Poly (phtalazinone) and copolymers Polyaniline and copolymers
 3. Polymer or oligomer containing sulfinate groups (P-(SO₂) nX) according to claims 1 and 2 characterized in that the polymer or oligomer is selected from the groups of (Hetero) aryl main chain polymers.
 4. Polymer or oligomer containing sulfinate groups (P-SO₂) nX) according to claims 1, 2 and 3 characterized in that the polymer or oligomer is selected from the groups of: Polyetherketones like polyetherketone PEK Victrex ®, polyetheretherketone PEEK Victrex ®, polyetheretherketoneketone PEEKK, polyetherketoneetherketoneketone PEKEKK Ultrapek ® Polyethersulfones like polysulfone Udel®, polyphenylsulfone Radel R®, Polyetherethersulfone Radel A®, polyethersulfone PES Victrex ®
 5. Polymer or oligomer containing sulfinate groups (P-(SO₂) nX) according to claims 1 to 4 characterized in that as reducing agents Zn dust, iron dust, sodium sulfit or other reducing sulfur salts as sodium dithionite, sodium thiosulfate or mixtures of these sulfur salts, Hydrazine, H₂S, LiAlH₄, triethylaluminium, ethylaluminium sesquichloride are used.
 6. Polymer or oligomer containing sulfinate groups (P-(SO₂) nX) according to claim 5 characterized in that as reducing agent sodium sulfit in solid form or as aqueous solution, Zn dust or LiAlH₄ in solid form or as solution in ether solvents are preferred.
 7. Process for the reduction of polymeric or oligomeric sulfinates P-(SO₂)_(n)X according to claims 1 to 6 characterized in that polymer or oligomer containing SO₂Y groups (Y═F, Cl, Br, I, OR, NR₂ (R=alkyl and/or aryl and/or H), (N imidazole, N pyrazole) is dissolved or suspended in a suitable organic solvent or in water, the reducing agent is added either dissolved or as a solid, diluted with organic solvent or water or pure (doppelt gemoppelt??), the reduction is conducted depending on reduction agent quantity and/or reduction time and/or reduction temperature completely or partially, and the formed polymer or oligomer containing sulfinate groups is isolated by precipitation in a suitable precipitation agent, if necessary hydrolysis of the remaining SO₂Y groups to sulfonate groups SO₃X by means of aqueous or nonacqueous base or acid solution, followed by dissolving in a dipolar aprotic solvent and again precipitation in a suitable precipitation agent and followed by filtration and drying.
 8. Process according to claim 7 characterized in that polymer or oligomer containing SO₂Y groups is dissolved or suspended in an ether solvent such as tetrahydrofurane or in water or alcohol.
 9. Process according to claims 7 and 8 characterized in that as a reducing agent LiAlH₄ dissolved in an ether solvent, such as tetrahydrofurane, is used.
 10. Process according to claims 7 to 9 characterized in that the reduction is carried out at temnperateres from −20° C. to −80° C.
 11. Process according to claims 7 to 10 characterized in that as a precipitation agent alcohols like methanol, ethanol or propanol or water are used.
 12. Process according to claims 7 to 10 characterized in that as dipolar aprotic solvents N-methylpyrrolidinone, N,N-diethylacetamnide or N,N-dimethylformamide, dimethylsulfoxide or sulfolane are used.
 13. Process according to claims 6 and 7 characterized in that the polymer or oligomer containing SO₂Y groups is dissolved or suspended in water, sodium sulfite or sodium dithionite or sodium thiosulfate is added as reducing agent as a solid or dissolved in water, the reduction is conducted depending on reduction agent quantity and/or reduction time and/or reduction temperature completely or partially, and the formed polymer or oligomer containing sulfinate groups is isolated by precipitation in a suitable precipitation agent, if necessary hydrolysis of the remaining SO₂Y groups to sulfonate groups SO₃X by means of aqueous or non-acqueous base or acid solution, followed by dissolving in a dipolar aprotic solvent and again precipitation in a suitable precipitation agent and followed by filtration and drying.
 14. Crosslinked polymers produced from partially or completely sulfinated polymers or oligomers according to claims 1 to 13 by addition of dihalogenoalkanes or oligohalogenoalkanes or other difunctional or oligofunctional alkylation agents like compounds with tosyl groups, epoxy groups to the solutions of polymers in dipolar aprotic solvents.
 15. Crosslinked polymer or polymer membrane or polymer(blend)membrane according to claim 14 characterized in that before the crosslinker is added to the solution of the partly or completely sulfinated polymer, still other if necessary functionalised polymers are added either dissolved or as a solid.
 16. Crosslinked polymer or polymer membrane or polymer(blend)membrane according to claims 1 to 15 characterized in that the polymers added to the sulfinated polymer containing polymer solution are selected from cation exchange polymers or their non-ionic precursors containing the cation exchange group SO₃H and/or PO₃H₂ and/or COOH and/or non-ionic precursors of the cation exchange group like SO₂Y and/or PO₂Y₂ or COY.
 17. Crosslinked polymer or polymer membrane or polymer(blend)membrane according to claims 1 and 14 to 16 characterized in that to the polymer solution containing the sulfinated polymer and if necessary other polymers apart from the difunctional or oligofunctional crosslinker simultaneously still other monofunctional alkylation agents are added, which can carry, if necessary, further functional groups, which are selected from: acidic groups: COOM, PO₃M₂, SO₃M with M=H or arbitrary cation; precursors of the acidic groups: COY, PO₂Y₂, SO₂Y; (Definition von Y??) basic groups like primary, secondary, tertiary amines, pyridine group, imidazole group, pyrazole group and these react simultaneously with the cross-inking reaction with sulfinate groups by alkylation.
 18. Use of membranes according to claims 1 to 17 for the generation of energy in an electrochemical way.
 19. Use of membranes according to claims 1 to 17 as a constituent of membrane fuel cells (hydrogen or direct methanol fuel cells) at temperatures of −20 to +180° C.
 20. Use of membranes according to claims 1 to 17 in electrochemical cells.
 21. Use of membranes according to claims 1 to 17 in secondary batteries.
 22. Use of membranes according to claims 1 to 17 in electrolysis cells.
 23. Use of membranes according to claims 1 to 17 in membrane separation processes like gas separation, pervaporation, perstraction, reverse osmosis, electrodialysis and diffusion dialysis. 